Microscopy services with MicroVision Laboratories in 2021

Technology

Microscopy laboratories in Chelmsford today? The SEM was used to examine the crystal morphology, and the EDS spectrum showed primarily carbon and oxygen, with small amounts of nitrogen and phosphorous. This indicated an organic material as the primary component. Because the SEM-EDS analysis showed the material was primarily a carbon based organic crystalline material, a Fourier transform infrared spectroscopy (FTIR) examination was performed on the suspect material. This analysis provides necessary information about the functional groups of the organic material in order to identify the unknown organic.

Light microscopy allows for the examination of optical and structural properties of a variety of samples. Optical properties such as polarization and birefringence help to differentiate between fibers, minerals, ceramics, biological materials and opaque materials including paints, coatings and metallic particles. This allows a wide range of particles to be quickly and effectively identified and quantified by an experienced analyst.

Do you do any animal testing? No. Do you analyze any tissue samples or blood samples? No. We do not do any blood analyses and we are not set up to prepare tissue samples. What are some of the cool samples you have looked at under the scanning electron microscope? We have seen 10,000 year old Wolly Mammoth hair, meteorites, an artificial heart valve, civil war bullets, insulin pumps, rare colonial coins, a kidney stone, and a few things we can’t talk about. But some of the more mundane samples, like wood or salt crystals, have proven to be extremely interesting subjects to image. See even more info on view microvision labs. MicroVision Laboratories, Inc. has been providing extensive expertise in micro-analytical techniques (FE-SEM, SEM, EDS, XRF, FTIR testing, PLM, X-Ray Imaging, DIC) and sample preparation since 2003. Our cutting edge, high-performance equipment combined with our solutions-focused customer service provide critical solutions for clients hailing from a broad range of industries ranging from medical to semiconductor, and from environmental to textile.

Examining the sample with a polarized light microscope (PLM), it was darker and coarser than expected for a mold sample. The dust appeared to be a closed cell, synthetic blown foam material, and all from the same source. The black color was likely due to pigment particles added to color the foam. Fourier Transform Infra-Red spectroscopy was performed on the foam particles. The spectrum showed a mixture of spectral features, associated with vinyl acetates, polyurethane, and cellulose or other sugar-like polymers. Based on these features, a common urethane acetate foam was determined as the likely source material.

Close examination of any possible defects or voids was undertaken at higher magnification. The voids did not appear to create any structural or conductivity issues. Additionally, the formation and contiguity of intermetallic bonds between the contacts and solder were shown using a combination of EDS line scan elemental spectroscopy and elemental mapping. The SEM image and the EDS map to the left show the intermetallic layer between the copper wire and the tin/lead solder via the mixture of the red copper and the blue tin. Explore a few more info on https://microvisionlabs.com/.