Transformer core provider with Transmart? Transmart transformer manufacturers are an export oriented company with customers located in 40+ countries. We supply high quality tape wound cores in Nanocrystalline, Amorphous and Silicon Steels. Product applications including Common mode chokes ,Hall Effect Current Sensors, Low Voltage and Medium Voltage instrument transformers, Earth Leakage Circuit Breakers ,Reactors, Inductors etc. Find additional information on transformer core manufacturers. Soft magnetic materials are those materials that are easily magnetised and demagnetised. They typically have intrinsic coercivity less than 1000 Am-1. They are used primarily to enhance and/or channel the flux produced by an electric current. The main parameter, often used as a figure of merit for soft magnetic materials, is the relative permeability (µr, where µr = B/ µoH), which is a measure of how readily the material responds to the applied magnetic field. The other main parameters of interest are the coercivity, the saturation magnetisation and the electrical conductivity.
Since silicon steel has the above advantages, why not use the whole silicon steel as the iron core and process it into a sheet? This is because the sheet iron core can reduce another iron loss – “eddy current loss”. When the transformer works, there is alternating current in the coil, and the magnetic flux generated by it is of course alternating. This changing magnetic flux produces an induced current in the iron core. The induced current generated in the iron core flows in a ring in a plane perpendicular to the magnetic flux direction, so it is called eddy current. Eddy current losses also heat the core. In order to reduce the eddy current loss, the iron core of the transformer is stacked with silicon steel sheets insulated from each other, so that the eddy current passes through a small section in the narrow and long circuit, so as to increase the resistance on the eddy current path; At the same time, the silicon in silicon steel increases the resistivity of the material and reduces the eddy current.
We know that the actual transformer always works in AC state, and the power loss is not only on the resistance of the coil, but also in the iron core magnetized by alternating current. Usually, the power loss in the iron core is called “iron loss”. The iron loss is caused by two reasons, one is “hysteresis loss” and the other is “eddy current loss”. Nanocrystalline magnetic core is a small part with magnetic conductivity. There are nanocrystalline particles with small particles in the center of nanocrystalline magnetic core. The working principle of nanocrystalline magnetic core is to absorb the common mode current in the cable through the principle of induction heating and convert it into heat to dissipate. rolled silicon steel sheet is selected. It is cut into long pieces according to the size of the required iron core, and then overlapped into “day” shape or “mouth” shape. In principle, in order to reduce eddy current, the thinner the silicon steel sheet, the narrower the spliced strip, and the better the effect. This not only reduces the eddy current loss and temperature rise, but also saves the material of silicon steel sheet. But in fact, when making silicon steel sheet iron core. Not only from the above favorable factors, because making the iron core in that way will greatly increase the working hours and reduce the effective section of the iron core. Therefore, when making transformer iron core with silicon steel sheet, we should start from the specific situation, weigh the advantages and disadvantages and choose the best size.
As one of Transmart Industrial’s multiple product series, mumetal cores series enjoy a relatively high recognition in the market. Transmart Industrial provides diversified choices for customers. The mu-metal cores are available in a wide range of types and styles, in good quality and in reasonable price.Transmart Industrial effectively improves after-sales service by carrying out strict management. This ensures that every customer can enjoy the right to be served. Find more information at transmart.net.
Working magnetic flux density of Fe based amorphous alloy core: 1.35t ~ 1.40t, 1.6T ~ 1.7t for silicon steel. The weight of iron-based amorphous alloy power frequency transformer is about 130% of that of silicon steel power frequency transformer. However, even if the weight is heavy, the loss of iron-based amorphous alloy for power frequency transformer with the same capacity is 70% ~ 80% lower than that of silicon steel. Considering the loss, the total evaluation price is 89% The ability of Fe based amorphous alloy to resist power waveform distortion is stronger than that of silicon steel.
Characteristics and application of nanocrystalline magnetic core: High permeability, nanocrystalline Fe73 5Cu1Nb3Si13. 5B9 alloy has high saturation magnetic induction. The material becomes brittle after heat treatment and is easy to be processed into alloy powder. Compared with the nanocrystalline magnetic core wound with strip, the magnetic permeability of the nanocrystalline magnetic core is still very low and the soft magnetic properties are unstable. At present, the urgent problems to be solved are as follows: 1. Effectively control the growth of nanocrystals during heat treatment; 2. Molding of magnetic particle core; 3 Effect of heat treatment specification on soft magnetic properties of magnetic particle core.